PENGARUH PENAMBAHAN LIMBAH SERBUK CANGKANG KERANG DAN SERBUK KACA SEBAGAI BAHAN PENGGANTI SEMEN TERHADAP KUAT TEKAN BETON NORMAL

Nurjanah Nurjanah, M. Dani Juli Rohman, Riski Krisdiantoro

Abstract


Abstrac

 

This research was conducted to determine the effect of the addition of waste shells and shell powder glass powder on the compressive strength of concrete. The method used is to use the experimental method by making test specimens with a mixture of waste shells powder shells and glass powder by 4%; 8%; 12% then compared with normal concrete without added ingredients. Concrete specimens that have been soaked then tested their compressive strength with the age of 7 days, 14 days, 21 days, and 28 days. The results of the test showed that normal concrete which was not added with the waste of shell powder and glass powder had compressive strength under mixed concrete variations of 4%, 8%, and 12 % when the concrete was 28 days old. Concrete which is added with waste of shell powder and glass powder has  a high yield at 4% variation that is equal to 20,66 MPa. For concrete Variasi of 8% has a compressive streng value of 20,17 MPa, For variations of 12% has a compressive strength value of 20,46 MPa and for normal concrete has a compressive strength of 20,16 MPa at the age 28 days. The compressive strength value generated by the research that occurs due to the slump test value factor that is done is not the same.

                      

Keywords: Concrete, scallop waste powder, Glass powder waste, concrete compressive strength.


Full Text:

XML

References


CW Kusuma.’’Pengertian Beton’’. 22 Juli 2018.

45 WIB.

http://digilib.unila.ac.id/2017/3/peng ertian-beton.html

Sugiyono, 2011. Metode Penelitian Kuantitaif Kualitatif dan R & B, Bandung: Alfabeta. Spector, I, Bertram & Zartman, William, I, 2003, Post- Agreement Negotiation Getting It Done and International Regimes,Washington, United States Institute of Peace.

Sartika,Dewi & Suci, “ Pengertian Beton Bertulang” 20 November 2017,

24 WIB

(https://www.coursehero.com/file/1 4330145/tugas-1/)

Anonim., 1991. SNI T-15-1990-03.’’ Tata Cara

Rencana Pembuatan Campuran Beton Normal’’ Departemen Pekerjaan Umum, Yayasan Lembaga Penyelidikan Masalah Bangunan, Bandung.

Imam Satyarno “Perencanaan Praktis Campuran Beton”2015

Dipohusodo, Istimawan, 1994. Struktur Beton Bertulang. Jakarta : PT. Gramedia Pustaka Utama.

DPU,1990, SK SNI T – 15 – 1990 – 03 Tata Cara

Pembuatan Rencana Campuran Beton Normal, Yayasan LPMB, Bandung.

Mulyono, T, 2004. Teknologi Beton, Andi, Yogyakarta

Peraturan Beton Bertulang Indonesia (PBI-1971), Departemen Pekerjaan Umum dan Tenaga Listrik, Bandung.

Standar Nasional Indonesia, SNI.T-08-1991-03 ( Standard Tata Cara Pengujian Kuat Tekan Beton ).

Tjokrodimulyo, Kardiyono, 2007.Teknologi beton. Biro penerbit jurusan teknik sipil fakultas Teknik UGM, Yogyakarta.

Gemelly Katrina “ Pemanfaatan Limbah Kulit Kerang Sebagai Subtitusi Pasir Dan Ampas Tebu Sebagai Subtitusi Semen Pada Campuran Beton Mutu K-225” 2014

Muhammad Hasbi Arbi “ Pengaruh Subtitusi Cangkang Kerang Dengan Agregat Halus Terhadap Kuat Tekan Beton” 2015

Hendra Purnomo & Endang Setyawati Hisam “ Pemanfaatan Serbuk Kaca Sebagai Subtitusi Parsial Semen Pada Campuran Beton Ditinjau Dari Kekuatan Tekan Dan Kekuatan Tarik Belah Beton”, 2014.

Johan Oberlyn Simanjuntak, ST., MT & Tiur Elita Saragi, ST., MT. “Hubungan Perawatan Beton Dan Kuat Tekan”, 2015.




DOI: http://dx.doi.org/10.33795/prokons.v14i1.233

Refbacks

  • There are currently no refbacks.


Copyright (c) 2020 Prokons: Jurnal Teknik Sipil



INDEXING : 

The following is an indexing list that includes the journal of the Prokons, published by the Civil Engineering Department, Politeknik Negeri Malang

    

    

_______________________________________________________________________________________________

Jurusan Teknik Sipil Politeknik Negeri Malang

Jalan Soekarno-Hatta No. 09, PO BOX 04 Malang 65141

Telp 0341-404424 || Fax 0341-404420

ISSN Print(1978-1784) || Online(2714-8815)

Email : prokons@polinema.ac.id

 

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.